Wire / Cable Scrape
Scrape Abrasion Kit
The Taber® Scrape Abrasion Kit enables you to use Taber's Linear Abraser Model 5750 and T-Slot Table (sold separately) to test the resistance to scrape abrasion of cables and wire. Based on ISO 6722, this accessory was designed to evaluate single-core cables, with a conductor size of 6 mm2 or less, intended for use in road vehicle applications. Note, the maximum diameter wire the holder will accommodate is approximately 6 mm diameter. Two attachments are provided with this kit permitting scrape abrasion with either the 0.25mm or 0.45mm diameter abrading wire.
A wire specimen approximately 1 m in length with approximately 25 mm of insulation removed from one end is secured to a "V-grooved" specimen holder. The appropriate scrape attachment is oriented perpendicular to the specimen. During the test, the scrape attachment traverses back and forth approximately 15 mm along the longitudinal axis of the wire specimen. Tests are operated at a speed of 55 ±5 cycles per minute. Two accessory weight discs are supplied to achieve the required load of 7N. (The Linear Abraser permits other test lengths, speeds and loads if desired.)
The abrading wire rubs the insulation until it wears through. Depending on material properties such as material hardness, flexural modulus and tensile strength, the oscillating wear of the abrading wire on the wire insulation typically results in plastic deformation and displacement; material fatigue (resulting in crack propagation); and / or micro-gouging. Once the abrading needle makes contact with the conductor, the test is automatically stopped. Results are reported as cycles to break-through.
Note: Studies have demonstrated that abrasion tends to be less severe if the insulation is thicker. This is because the contact area of the scrape needle is larger, and thus the stress or force applied in the contact area is reduced.
Wire Scrape Attachment
To determine the print durability (e.g. markings) on insulated wire or the influence of chemicals when performing a scrape test, Taber also offers the Wire Scrape Attachment. Used in conjunction with Taber's Reciprocating Abraser Model 5900, two attachments are offered with either a 1mm or 0.25mm diameter abrading needle (rod). The attachment is designed to secure an abrading needle (rod) such that it is oriented perpendicular to the axis of the wire specimen. An optional wire support fixture is available to secure specimen wires during testing.
Taber's Wire Scrape Attachment can be used to satisfy test method IEC 60794-1-2. This test method describes two procedures for conducting abrasion tests on fiber optic cable. Method E2A describes a test to measure the cable sheath's ability to withstand abrasion. The test abrades the surface of the cable approximately 10mm in length, at a frequency of 55 cycles per minute. Method E2B describes a test to measure the abrasion resistance for markings on cables. Option one is for rigid markings like embossing, indenting and sintering and utilizes the Wire Scrape Attachment with the 1mm diameter abrading rod. Option two is for other types of markings and utilizes a wool felt to be rubbed back and forth over the markings over a length of 100mm. For this option, the Taber CS-5 Jumbo Wearaser is suggested.
The Wire Scrape Attachment can also be used to satisfy MIL-STD-2223 Method 6004 to determine the durability of printed identification markings. This method utilizes the 0.025 inch diameter needle.
For tests that require an automatic stop when the insulation has been abraded to the wire, the Wire Scrape Attachment can also be used with Taber's Linear Abraser Model 5750 and Scrape Abrasion Kit (described above).